Raw materal omposition: High-quality modified peite, flating bead powde, slica sol. Production proces: after several raw materials are evenly stire in a high-speed mixer, they are put into a steel mold for pressing and forming. After demoulding, they are naturlly placed for a period of time and then baked at high temperature.
Compared with the traditional refractory insulation materials, it has the advantages of small thermal conductvity, small ensity, and can gretly reduce the cold suface temperature on the premise o the same thickness of the insulation layer, or reduce the thickness of the insulation layer on the premise that the cold surface temperature does not change.
| Model index | 0.35g/cm³ | 0.4g/cm³ | 0.5g/cm³ |
| Compressive strength at room temperature / Mpa≥ | 0.8 | 1.0 | 1.0 |
| Thermal conductivity (350±25℃)w/m.k≤ | 0.16 | 0.16 | 0.18 |
| 1000℃*6H Reburning line change≤ | 1% | 1% | 1% |